2300-1001 PEI玻璃纤维增强材料, 30% 填料按重量 基础创新塑料(美国)
2300-1001 PEI玻璃纤维增强材料, 30% 填料按重量 基础创新塑料(美国)
物性信息：
| 黄卡编号 | E121562-470961 E121562-221099 |
| 填料/增强材料 | 玻璃纤维增强材料, 30% 填料按重量 |
| 特性 | 符合 ECO |
| 机构评级 | EU Eco NSF 51 WRAS 未评级 |
| 加工方法 | 注射成型 |
| 多点数据 | Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Elastic Modulus vs Temperature (ASTM D4065) Flexural DMA (ASTM D4065) Instrumented Impact (Energy) (ASTM D3763) Instrumented Impact (Load) (ASTM D3763) Pressure-Volume-Temperature (PVT - Zoller Method) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835) |
| 比重 | 1.51 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (337°C/6.6 kg) | 5.0 | g/10 min | ASTM D1238 |
| 收缩率 | 内部方法 | ||
| 流动 : 3.20 mm | 0.20 到 0.40 | % | 内部方法 |
| 横向流动 : 3.20 mm | 0.20 到 0.40 | % | 内部方法 |
| 吸水率 | ASTM D570 | ||
| 24 hr | 0.16 | % | ASTM D570 |
| 平衡, 23°C | 0.90 | % | ASTM D570 |
| 洛氏硬度 (M 级) | 114 | ASTM D785 |
| 拉伸模量 1 | 9310 | MPa | ASTM D638 |
| 抗张强度 2 | ASTM D638 | ||
| 屈服 | 169 | MPa | ASTM D638 |
| 断裂 | 159 | MPa | ASTM D638 |
| 伸长率 3(断裂) | 3.0 | % | ASTM D638 |
| 弯曲模量 4(100 mm 跨距) | 8960 | MPa | ASTM D790 |
| 弯曲强度 5(断裂, 100 mm 跨距) | 228 | MPa | ASTM D790 |
| 悬壁梁缺口冲击强度 (23°C) | 85 | J/m | ASTM D256 |
| 无缺口悬臂梁冲击 (23°C) | 430 | J/m | ASTM D4812 |
| 反向缺口冲击 (3.20 mm) | 490 | J/m | ASTM D256 |
| 载荷下热变形温度 | ASTM D648 | ||
| 0.45 MPa, 未退火, 6.40 mm | 212 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 6.40 mm | 210 | °C | ASTM D648 |
| 维卡软化温度 | 228 | °C | ASTM D1525 6 |
| 线形热膨胀系数 - 流动 (-20 到 150°C) | 2.0E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 180 | °C | UL 746 |
| RTI Imp | 170 | °C | UL 746 |
| RTI | 180 | °C | UL 746 |
| 体积电阻率 | 3.0E+16 | ohms·cm | ASTM D257 |
| 介电强度 | ASTM D149 | ||
| 1.60 mm, in Air | 25 | kV/mm | ASTM D149 |
| 1.60 mm, in Oil | 30 | kV/mm | ASTM D149 |
| 介电常数 (1 kHz) | 3.70 | ASTM D150 | |
| 耗散因数 | ASTM D150 | ||
| 1 kHz | 1.5E-3 | ASTM D150 | |
| 2.45 GHz | 5.3E-3 | ASTM D150 | |
| 耐电弧性 7 | PLC 6 | ASTM D495 | |
| 相比耐漏电起痕指数(CTI) | PLC 4 | UL 746 | |
| 高电弧燃烧指数(HAI) | PLC 4 | UL 746 | |
| 高电压电弧起痕速率 (HVTR) | PLC 3 | UL 746 | |
| 热丝引燃 (HWI) | PLC 1 | UL 746 |
| UL 阻燃等级 | UL 94 | ||
| 0.254 mm | V-0 | UL 94 | |
| 1.22 mm | 5VA | UL 94 | |
| 极限氧指数 | 50 | % | ASTM D2863 |
| NBS Smoke Density - Flaming, Ds, 4 min | 1.60 | ASTM E662 |
| 干燥温度 | 149 | °C | |
| 干燥时间 | 4.0 到 6.0 | hr | |
| 干燥时间，Zui大 | 24 | hr | |
| 建议的Zui大水分含量 | 0.020 | % | |
| 建议注射量 | 40 到 60 | % | |
| 料筒后部温度 | 332 到 399 | °C | |
| 料筒中部温度 | 338 到 399 | °C | |
| 料筒前部温度 | 343 到 399 | °C | |
| 射嘴温度 | 343 到 399 | °C | |
| 加工（熔体）温度 | 349 到 399 | °C | |
| 模具温度 | 135 到 163 | °C | |
| 背压 | 0.345 到 0.689 | MPa | |
| 螺杆转速 | 40 到 70 | rpm | |
| 排气孔深度 | 0.025 到 0.076 | mm |